Heat capacities of kaolinite from 7 to 380 K and of DMSO- intercalated kaolinite from 20 to 310 K. The entropy of kaolinite Al2Si2O5(OH)4

Richard A. Robie·Bruce S. Hemingway
View original source ↗Export metadata ↓

Abstract

The heat capacities of kaolinite (7 to 380 K) and of dimethyl sulfoxide (DMSO) intercalated kaolinite (20 to 310 K) were measured by adiabatically shielded calorimetry. The third law entropy of kaolinite, S° 298 , is 200.9 ± 0.5 J ⋅ mol -1 ⋅ K -1 . The "melting point" of the DMSO in the intercalate, 288.0 ± 0.2 K, is 3.7 K lower than that of pure DMSO, 291.67 K. The heat capacity of DMSO in the intercalate above 290 K is approximately 5.2 J ⋅ mol -1 ⋅ K -1 smaller than that of pure liquid DMSO at the same temperature.

Explore related subjects

Clays and Clay MineralsArticle

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Richard A. Robie, Bruce S. Hemingway. 2024-04-02. Heat capacities of kaolinite from 7 to 380 K and of DMSO- intercalated kaolinite from 20 to 310 K. The entropy of kaolinite Al2Si2O5(OH)4. https://doi.org/10.1346/ccmn.1991.0390404

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related USGS reports

USGS2024

Structural charge site influence on the interlayer hydration of expandable three-sheet clay minerals

Previous investigations have demonstrated the influences of interlayer cation composition, relative humidity, temperature, and magnitude of interlayer surface charge on the interlayer hydration of montmorillonites and vermiculites. It has been suggested that the sites of layer charge deficiencies may also have an influence upon the amount of hydration that can take place in the interlayers of expandable clay minerals. If the interlayer cation-to-layer bonds are considered as ideally electrostatic, the magnitude of the forces resisting expansion may be expressed as a form of Coulomb's law. If this effect is significant, expandable structures in which the charge-deficiency sites are predominantly in the tetrahedral sheet should have less pronounced swelling properties than should structures possessing charge deficiencies located primarily in the octahedral sheet. Three samples that differed in location of layer charge sites were selected for study. An important selection criterion was a non-correlation between tetrahedral charge sites and high surface-charge density, and between octahedral charge sites and low surface-charge density. The effects of differences in interlayer cation composition were eliminated by saturating portions of each sample with the same cations. Equilibrium (001) d values at controlled constant humidities were used as a measure of the relative degree of interlayer hydration. Although no correlation could be made between the degree of interlayer hydration and total surface-charge density, the investigation does not eliminate total surface-charge density as being significant to the swelling properties of three-sheet clay-mineral structures. The results do indicate a correlation between more intense expandability and predominance of charge deficiencies in the octahedral sheet. Conversely, less intense swelling behavior is associated with predominantly tetrahedral charge deficiencies.

Clays and Clay Minerals↗
USGS2024

Surface area of montmorillonite from the dynamic sorption of nitrogen and carbon dioxide

Surface area determinations were made on a montmorillonite with various cations emplaced on the exchangeable sites, utilizing nitrogen and carbon dioxide as adsorbates at 77 ° K and 195 ° K, respectively, in a dynamic system. From the fraction of a Mississippi montmorillonite less than about 1 μ in size, samples were prepared by replacing the original exchangeable cations with Li + , Na + , K + , Rb + , Cs + , Mg ++ , Ca ++ , Ba ++ , and NH 4 + , forming a series of homoionic montmorillonite species. Surface areas from 3-point B.E.T. plots (half-hour adsorption points), with nitrogen as the adsorbate, ranged from 61 m 2 /g for Li-montmorillonite to 138 m 2 /g for Cs-montmorillonite, thus reflecting a certain degree of nitrogen penetration between layers. Complete penetration should theoretically result in a surface area of over 300 m 2 /g for this clay with a nitrogen monolayer between each pair of platelets. The experimental data indicate that the extent of penetration is time-dependent and is also a function of the interlayer forces as governed by the size and charge of the replaceable cation. This finding negates the generally accepted concept that nitrogen at 77 ° K does not penetrate the layers and provides a measure only of the external surface of expandable clay minerals. A further measure of the variation of interlayer forces is provided by the adsorption of carbon dioxide at 195 ° K. Surface area values ranged from 99 m 2 /g for Li-montmorillonite to 315 m 2 /g for Csmontmorillonite. Although the carbon dioxide molecule is larger than the nitrogen molecule, its greater penetration apparently is a result of its being kinetically more energetic (with a larger diffusion coefficient) at its higher adsorption temperature. Similar differences have been found with both adsorbates in the study of microporous substances, such as coal, where activated diffusion is of considerable significance.

Clays and Clay Minerals↗
USGS2024

Pedogenic formation of montmorillonite from a 2:1-2:2 intergrade clay mineral

Montmorillonite was found to be the dominant clay mineral in surface horizons of certain soils of the North Carolina Coastal Plain whereas a 2:1-2:2 intergrade clay mineral was dominant in subjacent horizons. In all soils where this clay mineral sequence was found, the surface horizon was low in pH (below 4 ⋅ 5) and high in organic matter content. In contrast, data from studies of other soils of this region (Weed and Nelson, 1962) show that: (1) montmorillonite occurs infrequently; (2) maximum accumulation of the 2:1-2:2 intergrade normally occurs in the surface horizon and decreases with depth in the profile; (3) organic matter contents are low; and (4) pH values are only moderately acid (pH 5-6). It is theorized that the montmorillonite in the surface horizon of the soils studied originated by pedogenic weathering of the 2:1-2:2 intergrade clay mineral. The combined effects of low pH (below 4 ⋅ 5) and high organic matter content in surface horizons are believed to be the agents responsible for this mineral transformation. The protonation and solubilization (reverse of hydrolysis) of Al-polymers in the interlayer of expansible clay minerals will occur at or below pH 4 ⋅ 5 depending on the charge and steric effects of the interlayer. A low pH alone may cause this solubilization and thus mineral transformation, but in the soils studied the organic matter is believed to facilitate and accelerage the transformation. The intermediates of organic matter decomposition provide an acid environment, a source of protons, and a source of watersoluble mobile organic substances (principally fulvic acids) which have the ability to complex the solubilized aluminum and move it down the profile. This continuous removal of solubilized aluminum would provide for a favorable gradient for aluminum solubilization. The drainage class or position in a catena is believed to be less important than the chemical factors in formation of montmorillonite from 2:1-2:2 intergrade, because montmorillonite is present in all drainage classes if the surface horizon is low in pH and high in organic matter.

Clays and Clay Minerals↗