Akermanite: phase transitions in heat capacity and thermal expansion, and revised thermodynamic data.

Abstract

A small but sharp anomaly in the heat capacity of akermanite at 357.9 K, and a discontinuity in its thermal expansion at 693 K, as determined by XRD, have been found. The enthalpy and entropy assigned to the heat-capacity anomaly, for the purpose of tabulation, are 679 J/mol and 1.9 J/(mol.K), respectively. They were determined from the difference between the measured values of the heat capacity in the T interval 320-365 K and that obtained from an equation which fits the heat-capacity and heat-content data for akermanite from 290 to 1731 K. Heat-capacity measurements are reported for the T range from 9 to 995 K. The entropy and enthalpy of formation of akermanite at 298.15 K and 1 bar are 212.5 + or - 0.4 J/(mol.K) and -3864.5 + or - 4.0 kJ/mol, respectively. Weak satellite reflections have been observed in hk0 single-crystal X-ray precession photographs and electron-diffraction patterns of this material at room T. With in situ heating by TEM, the satellite reflections decreased significantly in intensity above 358 K and disappeared at about 580 K and, on cooling, reappeared. These observations suggest that the anomalies in the thermal behaviour of akermanite are associated with local displacements of Ca ions from the mirror plane (space group P421m) and accompanying distortion of the MgSi2O7 framework.-L.C.C.