Hydrothermal reactivity of saponite

Saponite crystallizes from amorphous gel having an ideal saponite composition within 7 days at all experimental temperatures between 300° and 550°C at 1 kbar pressure. Reactions subsequent to this initial crystallization vary in type and degree, depending on the temperature of reaction and the type of interlayer cation. Above 450°C the intitially crystallized K-saponite dissolves, and talc and phlogopite nucleate and grow as discrete phases. At 450°C the initial K-saponite reacts to form talc and phlogopite layers, but the reaction proceeds via intracrystalline layer transformations rather than via dissolution and precipitation, producing a mixture of fully ordered, interstratified talc/saponite and fully ordered saponite/ phlogopite. The K-saponite shows subtle signs of reaction at 400°C after 200 days: this temperature is at least 150°C lower than experimental reaction temperatures previously reported for saponites. No reactions beyond the initial crystallization of saponite were observed below 400°C. K-saponite reacts more rapidly than either Na-saponite or Ca-saponite above 400°C and the Na-saponite and Ca-saponite produce no mica iayers during their transformation to mixed-layer clays. Interstratified talc/saponite formed in the Na-saponite system, and the Ca-saponite system produced both talc/saponite and chlorite/saponite.

Clays and Clay Minerals↗
USGS2024

Vanadium chlorite from a sandstone-hosted vanadium-uranium deposit, Henry basin, Utah

An unusual vanadium chlorite precipitated during the formation of a vanadium-uranium ore deposit in the Henry Basin, southeastern Utah. The ore deposit formed by reduction and precipitation of U and V in the presence of organic matter at the interface between a stagnant brine and overlying, circulating meteoric water. Some samples of the vanadium chlorite (heated before analysis) contain > 10% V 2 O 5 . In fresh samples, most of the vanadium is in the trivalent oxidation state. X-ray powder diffraction data suggest that Fe and V are concentrated preferentially in the interlayer hydroxide sheets of the chlorite. A d(060) value of 1.52 Å indicates that the chlorite probably has a dioctahedral structure which is distended by the presence of octahedral Fe and V. The vanadium ore zone is flanked by peripheral zones containing perfectly ordered chlorite/smectite. This chlorite/smectite contains much less V than the pure chlorite. This chlorite may have formed by the progressive precipitation of vanadium-rich interlayer hydroxide sheets in the mixed-layer chlorite/smectite in the most reducing portion of the ore zone. The pure chlorite is a IIb polytype, which, for nonvanadiferous analogs, is ordinarily found in high-temperature environments; however, no evidence exists to show that these rocks have ever been exposed to elevated temperatures. In fact, the presence of unreacted smectite in a potassium-rich setting and the low vitrinite reflectance of coalified plant debris indicate a low-temperature history for these sediments.

Utah↗
USGS2024

Changes in particle morphology during illitization: An experimental study

Smectite was reacted at several temperatures between 200°C and 500°C to produce interstratified illite/smectite (I/S) with different proportions of expandable layers. Dispersed and sedimented products were examined using a transmission electron microscope. Particle size and aspect ratio showed no systematic change as a function of reaction extent during R0 illitization. However, particles exhibited rounded edges during the early stages of the reaction, suggesting some dissolution of primary smectite. Additionally, increasing particle contrast in the electron beam suggests thickening of particles with increasing reaction extent. The thickening of particles is thought to be produced by the nucleation and precipitation of secondary illite layers on primary smectite layers. In the most extensively reacted I/S, particles have become aggregated into clumps or quasicrystals by lateral growth of illite layers. Internal uniformity of crystallographic alignment of individual growing crystals within each aggregate was reflected in the increasing frequency of 60° and 120° interfacial angles within each aggregate. In highly illitic I/S, these aggregates took on an overall euhedral form and became crystallographically contiguous, producing single crystal electron diffraction patterns.

Clays and Clay Minerals↗
USGS1992

Dioctahedral smectite reactions at elevated temperatures: Effects of K-availability, Na/K ratio and ionic strength

Hydrothermal experiments were conducted to measure the effects of K availability, Na / K ratio and ionic strength in chloride solutions on the rate and extent of the reaction of smectite to interstratified illite/smectite. The < 2 μm fraction of a bentonite was treated hydrothermally at temperatures of 200, 250, 300, 350, 400 and 450°C for run times of up to 30 days in the presence of 0.33, 0.66 and 1.00 equivalents of K per O 10 (OH) 2 . The effect of K-content on reaction progress is dramatic at low (0.33 eq.) K concentrations, but diminishes above a concentration of 0.66 equivalents. The effect of K-content is also more important at lower temperatures than at higher temperatures. Addition of K above that required to satisfy the cation exchange capacity of the smectite reduced the amount of chlorite byproduct and produced authigenic K-feldspar at the highest K-concentration. Similar experiments were run using Na / K equivalent ratios of 0 to 25 and total solution molalities of 0 to 3.75 molal. Because these experiments were small fixed-volume experiments, it was necessary to vary two of the three key variables (K-content, Na / K ratio, ionic strength simultaneously. The data suggest, however, that K-content has a much stronger effect than either Na / K ratio or ionic strength on illitization reaction progress.